target="_blank" rel="nofollow" href="#ulink_af4f4a83-a6c2-5792-a330-cf7a6f849587">1.25)The Guinier approximation is useful for systems containing non‐interacting particles (i.e. the structure factor S(q) = 1, see Section 1.5) and is typically valid for q < 1/Rg.
1.5 FORM AND STRUCTURE FACTORS
The total intensity scattered by an ensemble of particles (self‐assembled structures, surfactant or polymer assemblies, colloids, etc.) can be separated into terms depending on intra‐particle and inter‐particle terms (Figure 1.4), which are termed the form factor and structure factor, respectively.
Figure 1.4 Scattering within particles (from atoms/components shown as black dots) corresponds to form factor while scattering between particles (separated by vector rjk) corresponds to structure factor.
For a monodisperse system of spherically symmetric particles (number density np = N/V), the scattering can be written as
(1.26)
where F(q) is the amplitude of scattering from within a particle:
(1.27)
which is analogous to an isotropic average over Eq. (1.2).
Equation (1.25) can be separated into intra‐ and inter‐ particle components:
(1.28)
This can be written for the monodisperse ensemble of spherically symmetric particles as
(1.29)
Here the form factor is
(1.30)
and the structure factor is
(1.31)
In a sufficiently dilute system only the form factor needs to be considered. Intermolecular interferences are manifested by the increasing contribution of the structure factor as concentration is increased. In many micellar, biomolecular, and surfactant systems in dilute aqueous solution, structure factor effects may not be observed (over the typical q range accessed in most SAXS measurements). At high concentration, the structure factor is characterized by a series of peaks (due to successive nearest neighbour correlations, next nearest neighbour correlations etc.) the intensity decaying as q increases, oscillating around the average value S(q) = 1. The structure factor is related by a Fourier transform to the radial distribution function g(r):
(1.32)
where V is the volume of the particle.
Figure 1.5 shows the calculated total intensity within the monodisperse approximation (product of form and structure factors) for spheres of radius R = 30 Å (also hard sphere structure factor radius RH = 30 Å) at two volume fractions showing the increase in the contribution from the structure factor at low q including the development of a peak at q ≈ 0.1 Å−1.
Figure 1.5 Calculated total intensity I(q) = P(q)S(q) in the monodisperse approximation for spheres with radius R = 30 Å (polydispersity σ = 3 Å, see Figure 1.19) and hard sphere structure factor with RHS = 30 Å and volume fraction (a) 0.2, (b) 0.4. The structure factor S(q) has been scaled by a factor of 105 in (a) and 106 in (b) for ease of visualisation.
The preceding derivation (Eqs. (1.26)–(1.32))