consists of 33 parts of copper and 25 of zinc. It has a dark golden-yellow color, great tenacity, and can be forged at a red heat, properties which make it especially suitable for fine castings.
II.—Yellow.—Copper, 67 to 70 parts; zinc, 33 to 30 parts.
III.—Red.—Copper, 82 parts; zinc, 18 parts.
Copper Arsenic.
—Arsenic imparts to copper a very fine white color, and makes it very hard and brittle. Before German silver was known, these alloys were sometimes used for the manufacture of such cast articles as were not to come in contact with iron. When exposed to the air, they soon lose their whiteness and take on a brownish shade. On account of this, as well as the poisonous character of the arsenic, they are very little used at the present time. Alloys of copper and arsenic are best prepared by pressing firmly into a crucible a mixture of 70 parts of copper and 30 of arsenic (the copper to be used in the form of fine shavings) and fusing this mixture in a furnace with a good draught, under a cover of glass.
Copper Iron.
—The alloys of copper and iron are little used in the industries of the present day, but it would seem that in earlier times they were frequently prepared for the purpose of giving a considerable degree of hardness to copper; for in antique casts, consisting principally of copper, we regularly find large quantities of iron, which leads to the supposition that they were added intentionally.
These alloys, when of a certain composition, have considerable strength and hardness. With an increase in the quantity of the iron the hardness increases, but the solidity is lessened. A copper and iron alloy of considerable strength, and at the same time very hard, is made of copper, 66 parts; iron, 34. These alloys acquire, on exposure to air, an ugly color inclining toward black, and are therefore not adapted for articles of art.
Copper Nickel.
—A. Morrell, of New York, has obtained a patent on a nickel-copper alloy which he claims is valuable on account of its noncorrosive qualities, therefore making it desirable for ships, boiler tubes, and other uses where the metal comes much in contact with water. The process of making the metal is by smelting ore containing sulphide of nickel and copper, and besemerizing the resultant matter. This is calcined in order to obtain the nickel and copper in the form of oxides. The latter are reduced in reverberating furnace with carbon, or the like, so as to produce an alloy which preferably contains 2 parts of nickel and 1 part of copper.
Delta Metal.
—An alloy widely used for making parts of machinery, and also for artistic purposes, is the so-called Delta metal. This is a variety of brass hardened with iron; some manufacturers add small quantities of tin and lead; also, in some cases, nickel. The following analysis of Delta metal (from the factory at Düsseldorf) will show its usual composition:
| I | II | III | IV | V | |
|---|---|---|---|---|---|
| Copper | 55.94 | 55.80 | 55.82 | 54.22 | 58.65 |
| Zinc | 41.61 | 40.07 | 41.41 | 42.25 | 38.95 |
| Lead | 0.72 | 1.82 | 0.76 | 1.10 | 0.67 |
| Iron | 0.87 | 1.28 | 0.86 | 0.99 | 1.62 |
| Manganese | 0.81 | 0.96 | 1.38 | 1.09 | — |
| Nickel | traces. | traces. | 0.06 | 0.16 | 0.11 |
| Phosphorus | 0.013 | 0.011 | traces. | 0.02 | — |
I is cast, II hammered, III rolled, and IV hot-stamped metal. Delta metal is produced by heating zinc very strongly in crucibles (to about 1600° F.), and adding ferromanganese or “spiegeleisen,” producing an alloy of 95 per cent zinc and 5 per cent of iron. Copper and brass and a very small amount of copper phosphate are also added. {64}
Gong Metal.
—A sonorous metal for cymbals, gongs, and tam-tams consists of 100 parts of copper with 25 parts tin. Ignite the piece after it is cast and plunge it into cold water immediately.
Production Of Minargent.
—This alloy consists of copper, 500 parts; nickel, 350; tungsten, 25, and aluminum, 5. The metal obtained possesses a handsome white color and greatly resembles silver.
Minofor.
—The so-called Minofor metal is composed of copper, tin, antimony, zinc, and iron in the following proportions:
| I | II | |
|---|---|---|
| Copper | 3.26 | 4 |
| Tin | 67.53 | 66 |
| Antimony | 17.00 | 20 |
| Zinc | 8.94 | 9 |
| Iron | — | 1 |
Minargent and Minofor are sometimes used in England for purposes in which the ordinary Britannia metal, 2 parts tin and 1 part antimony, might equally well be employed; the latter surpasses both of them in beauty of color, but they are, on the other hand, harder.
Retz Alloy.
—This alloy, which resists the corrosive action of alkalies and acids, is composed of 15 parts of copper, 2.34 of tin, 1.82 of lead, and 1 of antimony. It can be utilized in the manufacture of receivers, for which porcelain and ebonite are usually employed.
Ruoltz